Buy ASTM D CLASSIFICATION SYSTEM FOR NYLON INJECTION AND EXTRUSION MATERIALS (PA) from SAI Global. ASTM D Standard Classification System for Nylon Injection and Extrusion Materials (PA). standard by ASTM International, 07/01/ View all product. 暂无评价|0人阅读|0次下载 | 举报文档. D – 01A Nylon Injection and Extrusion Materials_能源/化工_工程科技_专业资料。ASTM D标准.

Author: Tet Dokora
Country: Guinea-Bissau
Language: English (Spanish)
Genre: Sex
Published (Last): 15 March 2017
Pages: 416
PDF File Size: 19.15 Mb
ePub File Size: 9.51 Mb
ISBN: 186-7-93367-802-5
Downloads: 44131
Price: Free* [*Free Regsitration Required]
Uploader: Vibei

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every? It is possible, by agreement between the buyer and the seller, that materials incorporating other pigments or soluble stabilizers, or both, may prove adequate for particular applications.

D — 96a: Individual specimens shall not be removed from sealed containers until immediately before testing. Active view current version of standard. All tests shall be conducted on as-molded not annealed specimens conditioned dry-as-molded.

Flexural modulus shall be determined on Test Methods D test specimens 6. Q For general information not a requirement. J Carbon black content and absorbance must be 1.

Industrial & Engineering Plastics

A superscript epsilon e indicates an editorial change since the last revision or reapproval. An example of an unreinforced aatm material is given as follows: D If a speci? Current edition approved August 10, NOTE 9—An example of this classi? Weatherable nylon typically contains 1. If necessary, additional control of these reinforcements and additives can be accomplished by use of the suffix part of the system see Section 5.

  DE BELLIS MULTITUDINIS PDF

NOTE 6—Materials containing reinforcements or? Electrodes shall be American Standard D44066. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. G Izod impact for these materials shall be conducted on specimens with a NOTE 12—An example of a special material using this classi? This standard does not purport astj address all of the safety concerns, if any, associated with its use.

The designation PAG30A would indicate the following material requirements: Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.

In general, the suffix letter gives the general requirements needed and the? Suffix values will override the PA table values. There may be other requirements necessary to identify particular characteristics important to specialized applications.

ASTM D – 13 Standard Classification System for Nylon Injection and Extrusion Materials (PA)

The designation PAG35 indicates the following: Seven laboratories, including 3 U. The test specimen is a disk Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. The main property affected is ductility, as illustrated by a reduction in Izod impact and d44066 values.

  INSTALLATION ET CONFIGURATION DE SNMP SOUS UBUNTU PDF

Testing Conditions ISO This section may also include descriptions of the changes or reasons for the changes, or both. Selection of process temperature is made based on astmm major polymer component. The electrodes shall be inserted after the specimens have been conditioned.

I Groups 03 and 04 materials use Speci? Some of these compositions are also suitable for compression molding and application from solution.

D — 01a: Start the test within 2 min after removing the specimen and wiping with a dry cloth. Link to Active This link will always route to the current Active version of the standard.

Relative viscosity of Group 08 shall be measured on 9.